PTFE coated fiberglass Premium Series, designed for high request industry
PTFE coated fiberglass Premier Series YS9025AJ, using basic fiberglass fabric of 7628 coated with high quality PTFE formula. The final PTFE coated fabric has excellent smooth and high gloss surface, which has superior abrasion resistance and easy release property.
Applications of 0.25mm PTFE fiberglass fabric
PTFE coated Cloth provides a 100% non-stick surface for applications which need high temperature resistant, chemical resistant, easy release, low friction, insulation and so on.
Applications include release sheet for heat press machines, belting for food industry, Non stick baking liner or oven liner, electrical insulation and industrial processing.
0.25mm PTFE coated fiberglass is FDA & LFGB certificated, can be used in direct contact with food.
It is also widely used as a releasing sheet and laminating sheet for solar cell manufacturing, PVC or PE mold release, garment fusing, conveyor belt for paper industry, belting for tortilla and so on.
Properties of 0.25mm PTFE coated fiberglass
★ Non-stick and easy release
High gloss and low friction, result in excellent release property
★ Continuous working from -70°C – +260°C,
maximum working temperature is +327°C(short term).
★ Chemical resistant
★ Good welding property, can be easily made into belts with joint
★ Excellent tensile strength, makes the lifetime longer
Technical Data of YS9025AJ Teflon coated fiberglass fabric
|PTFE GLASS FABRIC||PREMIUM SERIES||PTFE(TEFLON)|
|Standard width |
Please ask for other widths
|1000, 1250, 1500,|
2000, 2600 mm
|39.5, 49.3, 59.1,
78.8, 102.4 inches
|Thickness||0.25 mm||0.0098 inches|
|Coated weight||530 g/m²||15.63 oz/yd²|
|PTFE content||62 %||62 %|
|Tensile strength||460 N/cm Warp||263 lbs/inches Warp|
|400 N/cm Warp||229 lbs/inches Fill|
|Temperature resistance||-73 to +260 °C||-100 to +500 °F|
Weight Tolerance g/m² = ±5
All technical data are based on average values. These values are based on test results we believes to be reliable, but they are not to be construed in any manner as warranties expressed.